Materials Research Bulletin , 2006, 41 (12), 2276-2285.

Photocatalytic performance of pure anatase nanocrystallite TiO2synthesized under low temperature hydrothermal conditions

Sayilkan, Funda | Erdemoglu, Sema | Asiltürk, Meltem | Akarsu, Murat | Sener, Sadiye | Sayilkan, Hikmet | Erdemoglu, Murat | Arpac, Ertugrul

Photocatalytic performance of a hydrothermally synthesized pure anatase TiO2with 8mm average crystalline size for decomposition of Reactive Red 141 was examined by investigating the effects of UV-light irradiation time, irradiation power, amount of TiO2and initial dye concentration. Change in the UV absorbance of the dye during irradiation was monitored. One wt.% TiO2in 30 mg/l Reactive Red 141 aqueous solution was found adequate for complete decolorization in 70 min at 770 W/m2irradiation power. It was realized that, compared to Degussa P-25, the synthesized nano-TiO2can be repeatedly used as a new catalyst. The results also proved that Reactive Red 141 is decomposed catalytically due to the pseudo first-order reaction kinetics.